An investigation on the environmental degradation of an ethylene– propylene copolymer was carried out through positron annihilation lifetime spectroscopy, density and differential scanning calorimetry measurements. Polymer sheets were exposed to sunlight up to 11000 hours. Density and melting enthalpy increase with ageing, while ortho-positronium intensity de- creases; ortho-positronium lifetime does not show significant variations up to 4400 hours. At higher exposures it starts to decrease. Outdoor ageing pro- duces an increased crystallinity of the copolymer; also a degradation occurs with formation of carbonyl groups. The corresponding Ps inhibition is the main reason for the decrease in ortho-positronium intensity, the other one being the reduced amount of the amorphous phase available. The lifetime decrease observed at the highest exposures can be interpreted in terms of a shrinking of the nanoholes trapping positronium.

Outdoor Ageing of an Ethylene–Propylene Copolymer: A Positron Annihilation Study

GALLO, Raffaele;
2005-01-01

Abstract

An investigation on the environmental degradation of an ethylene– propylene copolymer was carried out through positron annihilation lifetime spectroscopy, density and differential scanning calorimetry measurements. Polymer sheets were exposed to sunlight up to 11000 hours. Density and melting enthalpy increase with ageing, while ortho-positronium intensity de- creases; ortho-positronium lifetime does not show significant variations up to 4400 hours. At higher exposures it starts to decrease. Outdoor ageing pro- duces an increased crystallinity of the copolymer; also a degradation occurs with formation of carbonyl groups. The corresponding Ps inhibition is the main reason for the decrease in ortho-positronium intensity, the other one being the reduced amount of the amorphous phase available. The lifetime decrease observed at the highest exposures can be interpreted in terms of a shrinking of the nanoholes trapping positronium.
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11570/1915178
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus ND
  • ???jsp.display-item.citation.isi??? 0
social impact