Experimental tests have been carried out in order to investigate the influence of the heat treatments on the microstructures and mechanical properties of FV520B stainless steel. The fatigue strength of the common and heat-treated FV520B steels was rapidly assessed using the lock-in infrared thermographic methodology. Good agreements were achieved between the predicted values and those obtained by the traditional testing procedures. The temperature increments during the fatigue tests were tightly linked with the internal microstructural changes. The features of the fatigue fracture surface were observed by the scanning electron microscope. It is found that the fatigue microcracks were initiated from the corner of the specimen surface. The metallographic analysis shows that the improvement of the mechanical properties of FV520B steel is attributed to the formation of the fine-tempered martensite along with the secondary phase particles uniformly distributed at the grain boundary.

Influence of Heat Treatments on Mechanical Behavior of FV520B Steel

CRUPI, Vincenzo
Penultimo
;
GUGLIELMINO, Eugenio
Ultimo
2015-01-01

Abstract

Experimental tests have been carried out in order to investigate the influence of the heat treatments on the microstructures and mechanical properties of FV520B stainless steel. The fatigue strength of the common and heat-treated FV520B steels was rapidly assessed using the lock-in infrared thermographic methodology. Good agreements were achieved between the predicted values and those obtained by the traditional testing procedures. The temperature increments during the fatigue tests were tightly linked with the internal microstructural changes. The features of the fatigue fracture surface were observed by the scanning electron microscope. It is found that the fatigue microcracks were initiated from the corner of the specimen surface. The metallographic analysis shows that the improvement of the mechanical properties of FV520B steel is attributed to the formation of the fine-tempered martensite along with the secondary phase particles uniformly distributed at the grain boundary.
2015
File in questo prodotto:
File Dimensione Formato  
rivistaET_termografia.pdf

solo gestori archivio

Tipologia: Versione Editoriale (PDF)
Licenza: Tutti i diritti riservati (All rights reserved)
Dimensione 1.8 MB
Formato Adobe PDF
1.8 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11570/3052773
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 34
  • ???jsp.display-item.citation.isi??? 28
social impact