The anticorrosive properties of a silane-zeolite composite coating applied on a 6061 aluminum substrate was investigated. The composite film, deposited by dip-coating technique, was prepared with different contents of SAPO34 powder (60-90 wt%) with the purpose of evaluating the protective action offered by the zeolite-filled silane matrix. Corrosion protection performance, during immersion in 3.5% NaCl solution, was evaluated by means of a potentiodynamic polarization test and electrochemical impedance spectroscopy (EIS). The coating evidenced good barrier properties and high hydrophobicity. The addition of zeolite in the silane matrix induced, as expected, a reduction of cathodic and anodic current. The zeolite improved the barrier properties of the hybrid sol-gel films, enhancing the resistance to localized corrosion attacks. Better results were observed for the sample with 80 wt% of zeolite filler that evidenced still acceptable protective action after 3 days of immersion in the sodium chloride solution.

Electrochemical behavior of hydrophobic silane–zeolite coatings for corrosion protection of aluminum substrate

CALABRESE, Luigi;BONACCORSI, Lucio Maria;CAPRI', ANGELA;PROVERBIO, Edoardo
2014-01-01

Abstract

The anticorrosive properties of a silane-zeolite composite coating applied on a 6061 aluminum substrate was investigated. The composite film, deposited by dip-coating technique, was prepared with different contents of SAPO34 powder (60-90 wt%) with the purpose of evaluating the protective action offered by the zeolite-filled silane matrix. Corrosion protection performance, during immersion in 3.5% NaCl solution, was evaluated by means of a potentiodynamic polarization test and electrochemical impedance spectroscopy (EIS). The coating evidenced good barrier properties and high hydrophobicity. The addition of zeolite in the silane matrix induced, as expected, a reduction of cathodic and anodic current. The zeolite improved the barrier properties of the hybrid sol-gel films, enhancing the resistance to localized corrosion attacks. Better results were observed for the sample with 80 wt% of zeolite filler that evidenced still acceptable protective action after 3 days of immersion in the sodium chloride solution.
2014
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11570/3059217
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 44
  • ???jsp.display-item.citation.isi??? 40
social impact