In the present work, the comparison of the anti-corrosive properties of various types of zeolite based coatings, with different silane matrix on AA6061 aluminum substrates, are reported. High hydrophobicity, good adhesion and resistance to corrosion were observed for silane modified with the addition of SAPO-34 zeolite filler. Electrochemical impedance spectroscopy (EIS) tests were performed on all samples in a 3.5% (w/w) NaCI solution at increasing immersion times. All composite films showed good durability. Depending on the type of silane used as a matrix, the composite coating evidenced high stability up to one year of immersion.
Effect of silane matrix on corrosion protection of zeolite based composite coatings
CALABRESE, Luigi;BONACCORSI, Lucio Maria;CAPRI', ANGELA;PROVERBIO, Edoardo
2014-01-01
Abstract
In the present work, the comparison of the anti-corrosive properties of various types of zeolite based coatings, with different silane matrix on AA6061 aluminum substrates, are reported. High hydrophobicity, good adhesion and resistance to corrosion were observed for silane modified with the addition of SAPO-34 zeolite filler. Electrochemical impedance spectroscopy (EIS) tests were performed on all samples in a 3.5% (w/w) NaCI solution at increasing immersion times. All composite films showed good durability. Depending on the type of silane used as a matrix, the composite coating evidenced high stability up to one year of immersion.File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.