A systematic evaluation of mechanical and biocompatibility properties of different volume fractions of hydroxyapatite whiskers in comparison with three commercial dental composites filled with micro- and nanosilica particles was carried out. Six groups with different hydroxyapatite whiskers mass fractions were taken into account in order to be compared with the performances of silica particles based composites group. Flexural properties were evaluated via a universal testing machine (2.5 kN Zwick Line) with a 2 kN load-cell (sensitivity 0.001 N). The test was replicated 10 times for the seven experimental groups to better identify statically the significance of the mechanical performances data. MTT quantitative colorimetric assay was performed in order to evaluate the mitochondrial activity of living cells exposed to different resin composites. Data obtained show better interfacial interaction with filler/matrix until 20 wt% of hydroxyapatite whiskers partially replaced silica particles filler. After this threshold, the mechanical performances decrease dramatically due to both the hydroxyapatite agglomerates formation and the low degree of resin conversion. In addition, biocompatibility test showed less cytotoxic effect with the addition of 20 wt% of hydroxyapatite in comparison with higher rates.

Hydroxyapatite Whiskers Based Resin Composite versus Commercial Dental Composites: Mechanical and Biocompatibility Characterization

CALABRESE, Luigi;FABIANO, FRANCESCA;CURRO', MONICA;BORSELLINO, Chiara;FABIANO, Valerio;IENTILE, Riccardo;PROVERBIO, Edoardo
2016-01-01

Abstract

A systematic evaluation of mechanical and biocompatibility properties of different volume fractions of hydroxyapatite whiskers in comparison with three commercial dental composites filled with micro- and nanosilica particles was carried out. Six groups with different hydroxyapatite whiskers mass fractions were taken into account in order to be compared with the performances of silica particles based composites group. Flexural properties were evaluated via a universal testing machine (2.5 kN Zwick Line) with a 2 kN load-cell (sensitivity 0.001 N). The test was replicated 10 times for the seven experimental groups to better identify statically the significance of the mechanical performances data. MTT quantitative colorimetric assay was performed in order to evaluate the mitochondrial activity of living cells exposed to different resin composites. Data obtained show better interfacial interaction with filler/matrix until 20 wt% of hydroxyapatite whiskers partially replaced silica particles filler. After this threshold, the mechanical performances decrease dramatically due to both the hydroxyapatite agglomerates formation and the low degree of resin conversion. In addition, biocompatibility test showed less cytotoxic effect with the addition of 20 wt% of hydroxyapatite in comparison with higher rates.
2016
File in questo prodotto:
Non ci sono file associati a questo prodotto.
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11570/3096726
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 14
  • ???jsp.display-item.citation.isi??? 11
social impact