We have prepared novel nanohybrid Li2xMn1−xPS3/GO films consisting of graphene oxide (GO) and exfoliated MnPS3 nanosheets via an easy mixing protocol at room temperature. These films were investigated by SEM and AFM, as well as XRD, Raman and XPS spectroscopies, obtaining information about the nature of the interaction between MnPS3 and GO. In particular, the dark colour of the nanocomposite film and, more to the point, the analysis of (i) the C1s core level XPS spectra, (ii) the interlayer spacing obtained by XRD measurements and (iii) the increment in the intensity ratio ID/IG of the two bands typical of the carbon region of GO Raman spectra, suggest that a partial reduction of GO can be obtained right upon intercalation into Li2xMn1−xPS3.
Partial reduction of graphene oxide upon intercalation into exfoliated manganese thiophosphate
SILIPIGNI, Letteria
Primo
;BARRECA, Francesco;DE LUCA, Giovanna
;MONSU' SCOLARO, Luigi;
2017-01-01
Abstract
We have prepared novel nanohybrid Li2xMn1−xPS3/GO films consisting of graphene oxide (GO) and exfoliated MnPS3 nanosheets via an easy mixing protocol at room temperature. These films were investigated by SEM and AFM, as well as XRD, Raman and XPS spectroscopies, obtaining information about the nature of the interaction between MnPS3 and GO. In particular, the dark colour of the nanocomposite film and, more to the point, the analysis of (i) the C1s core level XPS spectra, (ii) the interlayer spacing obtained by XRD measurements and (iii) the increment in the intensity ratio ID/IG of the two bands typical of the carbon region of GO Raman spectra, suggest that a partial reduction of GO can be obtained right upon intercalation into Li2xMn1−xPS3.File | Dimensione | Formato | |
---|---|---|---|
Silipigni Phil.Mag. 2017,97(28),2484-2495.pdf
solo gestori archivio
Descrizione: Main text
Tipologia:
Versione Editoriale (PDF)
Licenza:
Tutti i diritti riservati (All rights reserved)
Dimensione
976.24 kB
Formato
Adobe PDF
|
976.24 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
3111734.pdf
solo utenti autorizzati
Descrizione: ARTICOLO PRINCIPALE
Tipologia:
Versione Editoriale (PDF)
Licenza:
Tutti i diritti riservati (All rights reserved)
Dimensione
6.94 MB
Formato
Adobe PDF
|
6.94 MB | Adobe PDF | Visualizza/Apri Richiedi una copia |
Pubblicazioni consigliate
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.