Mechanism of pitting corrosion of different Al alloys in anhydrous ethanol have been evidenced and discussed. Corrosion tests were carried out in an autoclave placed in a temperature controlled oil bath. It was observed that aluminum alloy characteristics greatly influence pitting activation and propagation mechanisms and morphologies. Better electrochemical stability was observed for AA6082 alloys. Instead intense corrosion phenomena were observed on AA5754 and AA5083 samples. Based on experimental results, a schemed model of the degradation stages of aluminum alloys surface during dry corrosion was proposed.

Pitting corrosion of aluminum alloys in anhydrous ethanol

Calabrese, Luigi
Primo
;
Bruzzaniti, Paolo
Secondo
;
Proverbio, Edoardo
Ultimo
Supervision
2018-01-01

Abstract

Mechanism of pitting corrosion of different Al alloys in anhydrous ethanol have been evidenced and discussed. Corrosion tests were carried out in an autoclave placed in a temperature controlled oil bath. It was observed that aluminum alloy characteristics greatly influence pitting activation and propagation mechanisms and morphologies. Better electrochemical stability was observed for AA6082 alloys. Instead intense corrosion phenomena were observed on AA5754 and AA5083 samples. Based on experimental results, a schemed model of the degradation stages of aluminum alloys surface during dry corrosion was proposed.
2018
File in questo prodotto:
File Dimensione Formato  
eTANOLO Calabrese_et_al-2018-Materials_and_Corrosion.pdf

solo gestori archivio

Descrizione: Articolo principale
Tipologia: Versione Editoriale (PDF)
Licenza: Tutti i diritti riservati (All rights reserved)
Dimensione 2.93 MB
Formato Adobe PDF
2.93 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11570/3131087
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 11
  • ???jsp.display-item.citation.isi??? 11
social impact