The aim of this study was to investigate the mechanical properties of a fiber hollow endodontic post characterized by the presence of an empty central cylindrical channel extended along the whole length. This particular shape allows clinicians to use the post also as a cementation resin carrier. Ten hollow posts were divided in two groups: the control group (unfilled hollow posts) (Group 0) and hollow posts filled with dual resin cement (Group 1). The samples of both groups were subjected to mechanical and micromorphological analysis by performing a three-point test and SEM observations. In the three-point test, the Group 1 samples exhibited a fracture load of 57.09 ± 5.06 N, a flexural strength of 1323.53 ± 110.09 MPa, and a Young's modulus of 42.87 ± 0.86 GPa. The samples of Group 2 exhibited a fracture load of 38.17 ± 1.7 N, a flexural strength of 908.87 ± 30.98 MPa, and a Young's modulus of 40.33 ± 1.9 GPa. The difference between fracture load, flexural strength, and deflection between the two groups was statistically highly significant (p < 0.01). Further, the difference between the Young's modulus of the two groups was statistically significant (p < 0.05). The values obtained are similar to those of other posts available on the market.

Evaluation of mechanical properties of a hollow endodontic post by three point test and SEM analysis: A pilot study

Lo Giudice G.
Primo
Conceptualization
;
Lo Giudice R.
Writing – Review & Editing
;
Puleio F.
Writing – Original Draft Preparation
;
Nicita F.
Penultimo
Data Curation
;
Calapaj M.
Ultimo
Formal Analysis
2019-01-01

Abstract

The aim of this study was to investigate the mechanical properties of a fiber hollow endodontic post characterized by the presence of an empty central cylindrical channel extended along the whole length. This particular shape allows clinicians to use the post also as a cementation resin carrier. Ten hollow posts were divided in two groups: the control group (unfilled hollow posts) (Group 0) and hollow posts filled with dual resin cement (Group 1). The samples of both groups were subjected to mechanical and micromorphological analysis by performing a three-point test and SEM observations. In the three-point test, the Group 1 samples exhibited a fracture load of 57.09 ± 5.06 N, a flexural strength of 1323.53 ± 110.09 MPa, and a Young's modulus of 42.87 ± 0.86 GPa. The samples of Group 2 exhibited a fracture load of 38.17 ± 1.7 N, a flexural strength of 908.87 ± 30.98 MPa, and a Young's modulus of 40.33 ± 1.9 GPa. The difference between fracture load, flexural strength, and deflection between the two groups was statistically highly significant (p < 0.01). Further, the difference between the Young's modulus of the two groups was statistically significant (p < 0.05). The values obtained are similar to those of other posts available on the market.
2019
File in questo prodotto:
File Dimensione Formato  
Evaluation_of_Mechanical_Properties_of_a_Hollow_En.pdf

accesso aperto

Descrizione: Articolo full text
Tipologia: Versione Editoriale (PDF)
Dimensione 3.24 MB
Formato Adobe PDF
3.24 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11570/3161430
Citazioni
  • ???jsp.display-item.citation.pmc??? 1
  • Scopus 9
  • ???jsp.display-item.citation.isi??? 9
social impact