Electrodes prepared by anodic oxidation of Ti foils are robust and not toxic materials for the electrocatalytic reduction of oxalic acid to glycolic acid, allowing the development of a renewable energy-driven process for producing an alcoholic compound from an organic acid at low potential and room temperature. Coupled with the electrochemical synthesis of the oxalic acid from CO2, this process represents a new green and low-carbon path to produce added value chemicals from CO2. Various electrodes prepared by anodic oxidation of Ti foils were investigated. They were characterized by the presence of a TiO2 nanotube array together with the presence of small patches, debris, or TiO2 nanoparticles. The concentration of oxygen vacancies, the amount of Ti3+ measured by X-ray photoelectron spectroscopy (XPS) and the intensity of the anodic peak measured by cyclic voltammetry, were positively correlated with the achieved oxalic acid conversion and glycolic acid yield. The analysis of the results indicates the presence of small amorphous TiO2 nanoparticles (or surface patches or debris) interacting with TiO2 nanotubes, the sites responsible for the conversion of oxalic acid and glycolic acid yield. By varying this structural characteristic of the electrodes, it is possible to tune the glycolic acid to glyoxylic acid relative ratio. A best cumulative Faradaic efficiency (FE) of about 84% with FE to glycolic acid around 60% and oxalic conversion about 30% was observed.

Electrocatalytic production of glycolic acid via oxalic acid reduction on titania debris supported on a TiO2 nanotube array

Francesco Pio Abramo
Primo
;
Federica De Luca
Secondo
;
Rosalba Passalacqua;Gabriele Centi;Gianfranco Giorgianni;Siglinda Perathoner
Penultimo
;
Salvatore Abate
Ultimo
2022-01-01

Abstract

Electrodes prepared by anodic oxidation of Ti foils are robust and not toxic materials for the electrocatalytic reduction of oxalic acid to glycolic acid, allowing the development of a renewable energy-driven process for producing an alcoholic compound from an organic acid at low potential and room temperature. Coupled with the electrochemical synthesis of the oxalic acid from CO2, this process represents a new green and low-carbon path to produce added value chemicals from CO2. Various electrodes prepared by anodic oxidation of Ti foils were investigated. They were characterized by the presence of a TiO2 nanotube array together with the presence of small patches, debris, or TiO2 nanoparticles. The concentration of oxygen vacancies, the amount of Ti3+ measured by X-ray photoelectron spectroscopy (XPS) and the intensity of the anodic peak measured by cyclic voltammetry, were positively correlated with the achieved oxalic acid conversion and glycolic acid yield. The analysis of the results indicates the presence of small amorphous TiO2 nanoparticles (or surface patches or debris) interacting with TiO2 nanotubes, the sites responsible for the conversion of oxalic acid and glycolic acid yield. By varying this structural characteristic of the electrodes, it is possible to tune the glycolic acid to glyoxylic acid relative ratio. A best cumulative Faradaic efficiency (FE) of about 84% with FE to glycolic acid around 60% and oxalic conversion about 30% was observed.
2022
File in questo prodotto:
File Dimensione Formato  
1-s2.0-S2095495621007063-main.pdf

solo utenti autorizzati

Descrizione: Versione Editoriale PDF
Tipologia: Versione Editoriale (PDF)
Licenza: Tutti i diritti riservati (All rights reserved)
Dimensione 2.31 MB
Formato Adobe PDF
2.31 MB Adobe PDF   Visualizza/Apri   Richiedi una copia
JECHEM.pdf

accesso aperto

Descrizione: Pre-print
Tipologia: Documento in Pre-print (manoscritto inviato all'editore, precedente alla peer review)
Licenza: Non specificato
Dimensione 2.5 MB
Formato Adobe PDF
2.5 MB Adobe PDF Visualizza/Apri
Pubblicazioni consigliate

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11570/3220074
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 21
  • ???jsp.display-item.citation.isi??? 20
social impact